• The forum upgrades have been completed. These were moderate security fixes from our software vendor and it looks like everything is working well. If you see any problems please post in the Forum Technical Support forum or email us at forum_moderator (at) aawforum.org. Thank you
  • February 2026 Turning Challenge: Cookie Jar! (click here for details)
  • Congratulations to Matt Carvalho for "Red Mallee Folded Form" being selected as Turning of the Week for February 9, 2026 (click here for details)
  • AAW Symposium demonstrators announced - If the 2026 AAW International Woodturning Symposium is not on your calendar, now is the time to register. And there are discounts available if you sign up early, by Feb. 28. Early Bird pricing gives you the best rate for our 40th Anniversary Symposium in Raleigh, North Carolina, June 4–7, 2026. (There are discounts for AAW chapter members too) For more information vist the discussion thread here or the AAW registration page
  • Welcome new registering member. Your username must be your real First and Last name (for example: John Doe). "Screen names" and "handles" are not allowed and your registration will be deleted if you don't use your real name. Also, do not use all caps nor all lower case.

Azobe new to me

Gerald Lawrence

Gerald Lawrence

Joined
Feb 6, 2010
Messages
3,492
Likes
2,582
Location
Brandon, MS
Website
threeringswoodshop.square.site
Had a opportunity presented to me at the last demo we did at the MS AG Museum. A volunteer whom I had talked to the month before brought me some wood and two pieces are Azobe.
For those who do not know (and I was one) it is a tropical wood from Africa and is used commonly as RR crossties. This wood is very hard at Janka 3220 just right at Ebony and dulls tools quickly. It has some open pore structure from which air would not remove the dust.. Sanded well but was a time consuming process. I gave up and buffed with Tripoli and Carnuba. This seemed to darken the pores and brought out a high shine.Azobe.jpg
 
Was in your area this past summer and went to the AG center. Interesting.
Our grandson played for the MS Braves. Don't know where he will be this season.
 
What is the grain orientation on your piece and what are the dimensions?
If it is big enough it would make a good utensil cup and if it were turned as an end grain piece it may have a whole different appearance.
 
Don Wattenhofer said:
What is the grain orientation on your piece and what are the dimensions?
If it is big enough it would make a good utensil cup and if it were turned as an end grain piece it may have a whole different appearance.
Click to expand...

This is turnerd side grain as was too small for end grain orientation. It is 3.5 inches tall. I have more that will be larger but not that much.
 
Gerald Lawrence said:
Had a opportunity presented to me at the last demo we did at the MS AG Museum. A volunteer whom I had talked to the month before brought me some wood and two pieces are Azobe.
For those who do not know (and I was one) it is a tropical wood from Africa and is used commonly as RR crossties. This wood is very hard at Janka 3220 just right at Ebony and dulls tools quickly. It has some open pore structure from which air would not remove the dust.. Sanded well but was a time consuming process. I gave up and buffed with Tripoli and Carnuba. This seemed to darken the pores and brought out a high shine.View attachment 31315
Click to expand...
Almost looks like palm...
 